For smoothing damp interiors based on innovative nanotechnology.
Prontoterm is an innovative smoothing level of the bottom of ready-to-use interior based on slaked lime and polymer siloxane.
It combines three characteristics: good conductivity, thermal, good reflection and thermal inertia thermal. Is able to reflect the heat and slow down the exchange of heat and to store heat due to its thermal mass, acts as a thermal flywheel, keeping the rooms more warm in the winter and cool in the summer.
Ideal as a cycle of shaving finishes, heat type ReflexIn.
Application
The product is a paste, the moist, ready-to-use.
The skim coat for internal damp is not to be mixed with cement, additives, or other substances in general.
For its application it is recommended that you enter a network of fiber reinforcement is glass.
ProntoTerm Finish lies initially with an american spatula, steel toothed, choosing the teeth in relation to the thickness that you want to get.
After the first layer of skim coat for internal damp, it adheres to the reinforcement mesh.
After having waited the necessary time, it should be run a second application using a straight blade to level the surface.
The minimum thickness to run is 3 mm/m2.
Greater thicknesses increase the insulating properties, but each individual layer should not exceed the thickness of 5 mm.
To obtain greater thicknesses it is necessary to make more layers of plaster for damp interiors, using guides.
In the case where the bracket will go later painting, it is necessary to frattazzare using a tool with a plastic or sponge before it arrives to the complete drying.
Before the finish coat you must wait for the complete drying, even at depth.
The time of drying of the levelling compound for internal wet areas is of at least 36 hours at 20° C for thicknesses of 5 mm.
The times can be increased according to the thickness applied and weather conditions.
If you are using ProntoTerm Finish to eliminate the thermal bridges resulting from pillars and beams, the product must be applied on all four sides, creating a thickness of 5 or 6 mm in order to prevent the problems of condensation.
The ideal temperature to apply the levelling compound for internal wet areas is between +5 and +30°C.
Up to the complete drying of the applied must be protected from frost, wind, rain and sun.
To prevent the formation of detachments and cracks is necessary to prevent rapid drying.
Technical Data
ProntoTerm Finish is a product of a paste, moist with a base of silicate mineral fiber reinforced, hydrated lime, cocciopesto, inert termoespansi, glass cell and light aggregates.
There are no reviews
ReflexIn, painting, heat-reflecting interior anti-mould, anti-condensation and breathable that by decreasing the dispersion of heat, it contributes to saving energy.
Additive with nanotechnology for concrete and other mixtures can increase the adhesion, elasticity and workability.
The bottom of the uniform heat-reflecting properties anchors for both internal and external.
The bottom of the uniform heat that can contribute to energy savings in buildings.
Primer for lime cycles pigmentabile smooth, suitable to the preparation of internal funds and external to the subsequent application of finishes
Special plaster finish or coating to a thickness of finish that improves the thermal performance of the buildings.
Sheath liquid elastomeric acrylic high quality with properties that reflect heat to the external surfaces.
Heat-reflecting film to the base of the beads and ceramics, and the particles nanoriflettenti dispersed in water.
Exterior paint, heat-reflecting based on siloxanic resins and special fillers, micro-and nano-sized useful to reduce the overheating of the walls in the summer phase, and to limit the heat loss in the winter phase
Smoothing level very low conductivity nanotechnology can improve the thermal performance of buildings.
Fixative a hardener composed of nanoparticles able to penetrate the material up to 20 mm.
Surface hardener for plaster posted particularly suitable for the consolidating treatment of mineral surfaces, peeling is not cohesive and absorbent.