PRONTOTERM FUND

PRONTOTERM FONDO

New product

100 Items

Smoothing level very low conductivity nanotechnology can improve the thermal performance of buildings.

126,00 € tax incl.

Prontoterm is an innovative smoothing level of the bottom of ready-to-use interior based on slaked lime and polymer siloxane.

It combines three characteristics: good conductivity, thermal, good reflection and thermal inertia thermal. Is able to reflect the heat and slow down the exchange of heat and to store heat due to its thermal mass, acts as a thermal flywheel, keeping the rooms more warm in the winter and cool in the summer.

Ideal as a cycle of shaving finishes, heat type ReflexIn.


Application

The product is a paste, the moist, ready-to-use.
The smoothing insulation is to be applied, spreading the first layer using a spatula steel toothed, choosing the teeth according to the thickness.
He then proceeds to attach the reinforcement mesh.
As soon as possible, you run a second application using a trowel with a straight blade to level the surface.
If the surface is then painted, the smoothing insulation applied, before it is completely dried, it must be frattazzato with a tool with a sponge or plastic.
Before applying ProntoTerm the surface must be wet thoroughly, and the operation must be repeated for the subsequent layers.
When you apply the smoothing insulation should not be exceeded thickness of 5 mm for each single layer.
If you want to obtain a greater thickness, it is necessary to apply several layers, helping with the guides.
ProntoTerm can be used to correct the thermal bridges due to columns and beams or to remove condensation, by applying the smoothing insulation on all four sides so as to form a thickness of 5/6 mm.
ProntoTerm is not to be mixed with cement, additives, or other substances in general.
Before applying on a large scale it is recommended to run preliminary tests to determine the amount of smoothing heat-insulating can be used.

Technical Data

  • Water mix: 24% ca
  • Particle size, bottom mix: grain size mixture the end of the ca. 1 mm ca. 0.3 mm.
  • Mass: dust ca. 550 kg/m3
  • Recommended thickness per layer: 5 mm
  • Minimum thickness: 3 mm/m2 flexural Strength: approx. 1,35 MPa
  • Compressive strength: 28 days Approx. 3.5 Mpa
  • Yield: approx. 0.6 kg/m2 x 1 mm. thick
  • Resistance to water vapour: µ = 9
  • Thermal conductivity: λ = 0.05 W/m°k
  • Thermal resistance: R= 0,45 (m2 K/W)
  • Mean coefficient of water absorption by capillarity
  • Classification according to 998-1:2010: water absorption by capillarity category W2 Cm to 0.1 (kg/m2 min 0,5)
  • Water vapor permeability (average): δ 2,2 10-11 (Kg/s m Pa)
  • The thickness of the air layer equivalent to water vapour diffusion (average) 0,15 Sd (m)